1.化学成份 |
|||||||||||||||||
|
合金牌号 |
C |
Cr |
Ni |
Fe |
Mo |
W |
Cu |
S |
P |
AL |
Ti |
Nb |
V |
Co |
SI |
Mn |
|
|
H.B |
≤0.07 |
≤1.00 |
余量 |
1.0~3.0 |
27.0~32.0 |
≤3.0 |
≤0.02 |
≤0.01 |
≤0.03 |
≤0.50 |
≤0.2 |
≤0.2 |
≤0.2 |
≤0.03 |
≤0.10 |
≤3.00 |
|
|
H.C-276 |
≤0.01 |
14.5~16.5 |
余量 |
4.0~7.0 |
15.0~17.0 |
3.0~4.5 |
|
≤0.03 |
≤0.04 |
|
|
|
≤0.35 |
≤2.5 |
≤1.00 |
≤1.00 |
|
|
Inconel 600 |
≤0.15 |
14.0~17.0 |
余量 |
6.0~10.0 |
|
|
≤0.50 |
|
|
|
|
|
|
|
≤0.50 |
≤1.00 |
|
|
Inconel 625 |
≤0.10 |
20.0~23.0 |
≥58.0 |
≤5.0 |
8.0~10.0 |
|
|
≤0.015 |
≤0.015 |
≤0.40 |
≤0.40 |
3.15~4.15 |
|
≤1.0 |
≤0.50 |
≤0.50 |
|
|
Incoloy800 |
≤0.10 |
19.0~23.0 |
30.0~35.0 |
余量 |
|
|
≤0.75 |
|
|
0.15~0.60 |
0.15~0.60 |
|
|
|
≤0.50 |
≤1.00 |
|
|
Incoloy 825 |
≤0.05 |
19.5~23.5 |
38.0~45.0 |
余量 |
2.5~3.5 |
|
1.5~3.0 |
|
|
≤0.20 |
0.60~1.20 |
|
|
|
≤0.50 |
≤1.00 |
|
|
Monel400 |
≤0.30 |
|
≥63.0 |
≤2.5 |
|
|
28.0 ~34.0 |
≤0.024 |
|
|
|
|
|
|
≤0.50 |
≤2.0 |
|
|
MonelK500 |
≤0.18 |
|
≥63.0 |
≤2.0 |
|
|
27.0-33.0 |
≤0.01 |
|
2.3-3.15 |
0.35-0.85 |
|
|
|
≤0.50 |
≤1.50 |
|
|
2.常温下合金的 机械性能 |
3.部分合金牌号中美对照 |
||||||||||||||||
|
合金牌号 |
热处理规范 及温度(℃) |
机械性能 |
适用范围 |
密度 |
中国牌号 |
美国牌号 |
|||||||||||
|
固溶处理 |
抗拉强度Rm N/mm2 |
屈服强度Rm N/mm2 |
伸长率A5% |
硬度 |
适用介质 |
适用温度 |
0Ni65Mo28F35V(NS321) |
Hastelloy B |
|||||||||
|
H.B |
1140~1190 |
≥690 |
≥283 |
≥40 |
|
耐强还原性腐蚀介质,如热浓盐酸,硫酸，磷酸及氯化氢气体等 |
≤371℃ |
8.8g/cm3 |
0Cr15Ni60Mo16W5Fe5(NS333) |
Hastelloy C |
|||||||
|
H.C-276 |
1160~1210 |
≥690 |
≥283 |
≥40 |
|
耐卤蔟及其化合物腐蚀,如乙烯，氯化物，氢氟酸等 |
≤538℃ |
8.9g/cm3 |
1Cr15Ni75Fe8(NS312) |
Inconel 600(N06600) |
|||||||
|
Inconel 600 |
1000~1050 |
550 |
240 |
30 |
≤160HV |
耐高温氧化物介质 |
-240～650℃ |
8.4g/cm3 |
0Cr20Ni65Mo10Nb4(NS336) |
Inconel 625(N06625) |
|||||||
|
Inconel 625 |
1100~1150 |
≥760 |
≥345 |
≥30 |
≤220HB |
耐氧化-还原复合介质，耐海水腐蚀，且热强度高 |
-240～650℃ |
8.4g/cm3 |
0Cr20Ni32AlTi(NS111) |
Inconel 800(N08800) |
|||||||
|
Incoloy800 |
1000~1060 |
≥500 |
≥210 |
≥35 |
|
抗氧化性介质腐蚀，高温下抗渗碳性良好 |
-240～650℃ |
8.08g/cm3 |
65Ni-34Cu |
Monel400(N04400) |
|||||||
|
Incoloy 825 |
1000~1050 |
≥586 |
≥241 |
≥30 |
≤200HB |
耐氧化物应力腐蚀及氧化-还原复合介质腐蚀(多种离子的硫酸环境) |
-240～650℃ |
8.1g/cm3 |
0Cr21Ni42Mo3Cu2Ti |
Inconel 825(N08825) |
|||||||
|
Monel400 |
1000~1070 |
≥480 |
≥170 |
≥35 |
|
碱、盐、食品、不含空气的酸溶液，氢氟酸等 |
-240～482℃ |
8.83g/cm3 |
注：除Monel材料外，其余材料化学成分及机械性能来源于GB/T15007-94和GB/T15008-94 |
||||||||
|
Monel K500 |
1000~1070 |
≥1000 |
≥790 |
≥20 |
≥27 |
-240～482℃ |
8.85g/cm3 |
||||||||||